1.4404
316L
SUS316L
022Cr17Ni12Mo2
Exhaust manifolds /Furnace parts /Heat exchangers
|
| |
316L stainless steel is a low carbon version of 316 (L = Low Carbon), which is an austenitic stainless steel. Due to its excellent corrosion resistance, good welding performance and high cleanliness, it is widely used in the chemical, marine, medical and food fields, especially in situations where heat treatment cannot be performed after welding.
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N |
| GB/T 3280-2015 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| JIS G 4305 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | |
| ASTM A240 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 485 | 180 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 480 | 175 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 485 | 170 | 40 | 217 | 95 | ------ | |||
| 316L | |||||||||
| Thickness | 0.05-3mm | ||||||||
| Width | 4.6-1500mm | ||||||||
| Length | As required | ||||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | ||||||||
| Original | DSM | ||||||||
| Standard | Produce as per your requirement. | ||||||||
| MOQ | 2tons.We also can accept sample order. | ||||||||
316L stainless steel is a low carbon version of 316 (L = Low Carbon), which is an austenitic stainless steel. Due to its excellent corrosion resistance, good welding performance and high cleanliness, it is widely used in the chemical, marine, medical and food fields, especially in situations where heat treatment cannot be performed after welding.
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N |
| GB/T 3280-2015 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| JIS G 4305 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | |
| ASTM A240 | 0.03 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 485 | 180 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 480 | 175 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 485 | 170 | 40 | 217 | 95 | ------ | |||
| 316L | |||||||||
| Thickness | 0.05-3mm | ||||||||
| Width | 4.6-1500mm | ||||||||
| Length | As required | ||||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | ||||||||
| Original | DSM | ||||||||
| Standard | Produce as per your requirement. | ||||||||
| MOQ | 2tons.We also can accept sample order. | ||||||||