1.4571
316Ti
SUS316Ti
06Cr17Ni12Mo2Ti
Has good corrosion resistance, used to resist sulfuric acid, acid formate acetic acid equipment
|
| |
316Ti stainless steel is an austenitic stainless steel with titanium (Ti) added, which is an improvement on 316. Its main advantages are: improved high temperature strength and intergranular corrosion resistance, especially suitable for structural parts in high temperature welding or long-term use in 550°C~800°C temperature environment.
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N | Others |
| GB/T 3280 | 0.08 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | Ti≥5XC | |
| JIS G 4305 | 0.08 | 1.0 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | Ti:5XC% min | |
| ASTM A240 | 0.08 | 1.0 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 | Ti:5X(C+N)min,0.70max |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 515 | 205 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 520 | 205 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 515 | 205 | 40 | 217 | 95 | ------ | |||
Application:
Has good corrosion resistance, used to resist sulfuric acid, acid formate acetic acid equipment.
Size:thickness from 0.1mm-0.5mm is available ,width from 4.6-600mm is available.
316Ti stainless steel is an austenitic stainless steel with titanium (Ti) added, which is an improvement on 316. Its main advantages are: improved high temperature strength and intergranular corrosion resistance, especially suitable for structural parts in high temperature welding or long-term use in 550°C~800°C temperature environment.
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | Mo | N | Others |
| GB/T 3280 | 0.08 | 0.75 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | Ti≥5XC | |
| JIS G 4305 | 0.08 | 1.0 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | Ti:5XC% min | |
| ASTM A240 | 0.08 | 1.0 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | 2.00-3.00 | 0.1 | Ti:5X(C+N)min,0.70max |
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | ||||
| Mpa | Mpa | 50mm | HBW | HRB | HV | ||||
| GB/T 3280-2015 | 515 | 205 | 40 | 217 | 95 | 220 | ------ | ||
| JIS G 4305 | 520 | 205 | 40 | 187 | 90 | 200 | ------ | ||
| ASTM A240 | 515 | 205 | 40 | 217 | 95 | ------ | |||
Application:
Has good corrosion resistance, used to resist sulfuric acid, acid formate acetic acid equipment.
Size:thickness from 0.1mm-0.5mm is available ,width from 4.6-600mm is available.