High quality hot sales products hot rolled 5Cr15Mov stainless steel sheet/plate .Martensitic stainless steels exhibit an excellent combination of mechanical resistance and hardness by the suitable thermal treatment. Moreover, they are ductile and can be shaped. Due to its high molybdenum and chromium content 5Cr15MoV has the best corrosion resistance among this family of stainless steel.
Cutting tools/High quality knives/Cutlery
Wash the surface with neutral soap and water applied with a cloth or a brush without scratching the stainless steel. Then, always rinse the stainless steel with water to remove completely the cleaning agent. Finally, it is recommended to dry the surface to preserve a good superficial condition. In severe environments, a frequent cleaning is strongly recommended.High quality hot sales products hot rolled 5Cr15Mov stainless steel sheet/plate.
Chemical Composition:
| C≤% | Mn≤% | P≤% | S≤% | Si≤% | Cr% | Mo≤% | V |
| 0.45-0.55 | 1.00 | 0.040 | 0.015 | 1.00 | 12.00-14.00 | 0.50-0.80 | 0.10-0.20 |
Performance:
| T.S. min | Y.S. min | EL min% | HARDNESS( max) | ||
| Mpa | Mpa | 50mm | HBW | HRB | HV |
| 850 | 12 | 280 | 100 | 280 | |
5Cr15Mov/1.4116
standard：
ASTM-A240
BS EN 10088
GBT 3280/4237
JIS G 4305
High quality hot sales products hot rolled 5Cr15Mov stainless steel sheet/plate .Martensitic stainless steels exhibit an excellent combination of mechanical resistance and hardness by the suitable thermal treatment. Moreover, they are ductile and can be shaped. Due to its high molybdenum and chromium content 5Cr15MoV has the best corrosion resistance among this family of stainless steel.
Cutting tools/High quality knives/Cutlery
Wash the surface with neutral soap and water applied with a cloth or a brush without scratching the stainless steel. Then, always rinse the stainless steel with water to remove completely the cleaning agent. Finally, it is recommended to dry the surface to preserve a good superficial condition. In severe environments, a frequent cleaning is strongly recommended.High quality hot sales products hot rolled 5Cr15Mov stainless steel sheet/plate.
Chemical Composition:
| C≤% | Mn≤% | P≤% | S≤% | Si≤% | Cr% | Mo≤% | V |
| 0.45-0.55 | 1.00 | 0.040 | 0.015 | 1.00 | 12.00-14.00 | 0.50-0.80 | 0.10-0.20 |
Performance:
| T.S. min | Y.S. min | EL min% | HARDNESS( max) | ||
| Mpa | Mpa | 50mm | HBW | HRB | HV |
| 850 | 12 | 280 | 100 | 280 | |