304 is an austenitic stainless steel with a nominal composition of 17 percent chromiumand 7 percent nickel,which provides good strength and ductility when cold worked.lt alsohas excellent corrosion resistance properties 304 is well suited to welding and forming anddrawing.304 stainless steel is an austenitic stainless with excellent corrosion resistance.Precision Steel stocks 304 stainless steel in the 1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
| GBT | JIS | ASME | BS EN |
| 06Cr19Ni10 | SUS304 | 304 | 1.4301 |
Chemical Analysis
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | N |
| GB/T 3280-2015 | 0.07 | 0.75 | 2 | 0.045 | 0.03 | 8.00-10.50 | 17.50-19.50 | 0.1 |
| JIS G 4305 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | - |
| ASTM A240 | 0.08 | 0.75 | 2 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | 0.1 |
Mechanical Properties
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | |||
| Mpa | Mpa | 50mm | HBW | HRB | HV | |||
| GB/T 3280-2015 | 515 | 205 | 40 | 201 | 92 | 210 | - | |
| JIS G 4305 | 520 | 205 | 40 | 207 | 95 | 218 | - | |
| ASTM A240 | 515 | 205 | 40 | 201 | 92 | - | - | |
DSM production capacity
| Thickness | 0.05-3mm | |||||||
| Width | 4.6-1500mm | |||||||
| Length | As required | |||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | |||||||
| Original | DSM | |||||||
| Standard | Produce as per your requirement. | |||||||
| MOQ | 2tons.We also can accept sample order. | |||||||
| Application | It is widely used in New energy, automobile, chemical plant, shipbuilding, textile, home appliance, railways, pressurized containers, constructions, medical equipment, electronics, flatware. | |||||||
Applications
Food equipment
general chemical equipment
atomic energy industry
| Physical Properties of Stainless Steel 304 | |
| Density(kg/dm3) 20℃ | 7.93 |
| Melting Range ℃ | 1398~1454°C |
| Specific Heat {kJ/(kg·K)} | 0.5 |
Thermal Conductivity {W/(m·K)} 100℃ | 100℃ 16.3 500℃ 21.5 |
| Linear expansion coefficient(10-6/K) | 0℃~100℃ 17.2 0℃~500℃ 18.4 |
Electrical Resistivity (Ω·mm2/m) 20℃ | 0.73 |
| Longitudinal Modulus of Elasticity(kN/mm2) 20℃ | 193 |
304 Stainless Steel
304 is an austenitic stainless steel with a nominal composition of 17 percent chromiumand 7 percent nickel,which provides good strength and ductility when cold worked.lt alsohas excellent corrosion resistance properties 304 is well suited to welding and forming anddrawing.304 stainless steel is an austenitic stainless with excellent corrosion resistance.Precision Steel stocks 304 stainless steel in the 1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
| GBT | JIS | ASME | BS EN |
| 06Cr19Ni10 | SUS304 | 304 | 1.4301 |
Chemical Analysis
| Standard | C≤% | Si≤% | Mn≤% | P≤% | S≤% | Ni≤% | Cr% | N |
| GB/T 3280-2015 | 0.07 | 0.75 | 2 | 0.045 | 0.03 | 8.00-10.50 | 17.50-19.50 | 0.1 |
| JIS G 4305 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | - |
| ASTM A240 | 0.08 | 0.75 | 2 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | 0.1 |
Mechanical Properties
| Standard | T.S. min | Y.S. min | EL min% | HARDNESS( max) | BEND | |||
| Mpa | Mpa | 50mm | HBW | HRB | HV | |||
| GB/T 3280-2015 | 515 | 205 | 40 | 201 | 92 | 210 | - | |
| JIS G 4305 | 520 | 205 | 40 | 207 | 95 | 218 | - | |
| ASTM A240 | 515 | 205 | 40 | 201 | 92 | - | - | |
DSM production capacity
| Thickness | 0.05-3mm | |||||||
| Width | 4.6-1500mm | |||||||
| Length | As required | |||||||
| Surface | 2B，NO.4，BA，4K，HL，8K,SB | |||||||
| Original | DSM | |||||||
| Standard | Produce as per your requirement. | |||||||
| MOQ | 2tons.We also can accept sample order. | |||||||
| Application | It is widely used in New energy, automobile, chemical plant, shipbuilding, textile, home appliance, railways, pressurized containers, constructions, medical equipment, electronics, flatware. | |||||||
Applications
Food equipment
general chemical equipment
atomic energy industry
| Physical Properties of Stainless Steel 304 | |
| Density(kg/dm3) 20℃ | 7.93 |
| Melting Range ℃ | 1398~1454°C |
| Specific Heat {kJ/(kg·K)} | 0.5 |
Thermal Conductivity {W/(m·K)} 100℃ | 100℃ 16.3 500℃ 21.5 |
| Linear expansion coefficient(10-6/K) | 0℃~100℃ 17.2 0℃~500℃ 18.4 |
Electrical Resistivity (Ω·mm2/m) 20℃ | 0.73 |
| Longitudinal Modulus of Elasticity(kN/mm2) 20℃ | 193 |