304
DSM
1.4301
304
SUS304
06Cr19Ni10
Food equipment, general chemical equipment, atomic energy industry
Product Description
304 is an austenitic stainless steel with a nominal composition of 17 percent chromiumand 7 percent nickel,which provides good strength and ductility when cold worked.lt alsohas excellent corrosion resistance properties 304 is well suited to welding and forming anddrawing.304 stainless steel is an austenitic stainless with excellent corrosion resistance.Precision Steel stocks 304 stainless steel in the 1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
Chemical Composition
| C | Si | Mn | P | S | Cr | Ni |
| ≤0.070 | ≤0.75 | ≤2.00 | ≤0.040 | ≤0.015 | 17.50-19.00 | 8.00-10.00 |
Mechanical properties
| Hardness | Tensile strength(Min) | Yield Strength(Min) | Elongation(Min)% | Hardness | ||
| Mpa | Mpa | ＜0.4mm | 0.4-0.8mm | ≥0.8mm | HV(Min） | |
| 1/2 H | 860 | 515 | 10 | 10 | 12 | 250 |
| 3/4 H | 1035 | 760 | 6 | 7 | 7 | 310 |
| Applications | Tableware /Household appliances /Industry /Construction /decoration | ||||||||
| Mechanica Properties After Cold Rolling and Final Annealing | Rp0.2 | > 230 N/mm2 | |||||||
| Rm | 540 - 750 N/mm2 | ||||||||
| Elongation | > 45% | ||||||||
| Hardness | < 200 HB | ||||||||
| Physical Properties | 20℃ | 100℃ | 200℃ | 300℃ | 400℃ | 500℃ | |||
| Modulus of elasticity (GPa) | 200 | 194 | 186 | 179 | 172 | 165 | |||
| Mean coefficient of linear expansion between 20℃ (10-6 x K-1) and | - | 16 | 16.5 | 17 | 17.5 | 18 | |||
| Thermal conductivity (W/m·K) | 15 | 17 | 18 | 19 | 20.5 | 22 | |||
| Electrical resistivity (Ω·mm2/m) | 0.73 | 0.8 | 1 | 1.15 | 1.22 | 1.25 | |||
| WELDING | 304 is suitable for all conventional welding techniques.This grade does not require thermal treatment after welding. | N/A | |||||||
| PITTING CORROSION | 304 is successfully used in media where chloride concentration does not exceed 200 ppm. | N/A | |||||||
| CORROSION RESISTANCE | 304 shows good corrosion resistance in a wide range of applications. As an example, 304 exhibits corrosion rates lower than 0.10 mm/year in the following media: -20% acetic acid at 800C. -90% formic acid at 200C. -20% phosphoric acid at 600C. -20% nitric acid at 500C. -90% sulphuric acid at 200C. -Toluene. -Milk. -Beer. -Juice. -Wine. | ||||||||
| SURFACE CLEANING | Wash the surface with neutral soap and water applied with a cloth or a brush without scratching the stainless steel. Then, always rinse the stainless steel with water to remove completely the cleaning agent. Finally, it is recommended to dry the surface to preserve a good superficial condition. In severe environments, a frequent cleaning is strongly recommended. | ||||||||
| SPECIFICATIONS | 304 can be delivered according to EN, ASTM, ASME, AMS, QQS and MILS standard requirements. | ||||||||
| 304 is approved in compliance with: -PED (Pressure Equipment Directive), DGRL 97/23/EG according to EN 10028-7 and AD2000 Merkblatt W2 and W10. -Lloyd´s Register of Shipping. | |||||||||
| It complies with the European Directives: -Food industry, RE 1935/2004. -Hexavalent chromium, ROHS. -Electrical instruments, ROHS. | |||||||||
Product Description
304 is an austenitic stainless steel with a nominal composition of 17 percent chromiumand 7 percent nickel,which provides good strength and ductility when cold worked.lt alsohas excellent corrosion resistance properties 304 is well suited to welding and forming anddrawing.304 stainless steel is an austenitic stainless with excellent corrosion resistance.Precision Steel stocks 304 stainless steel in the 1/4 hard, 1/2 hard, 3/4 hard, full hard, and extra hard tempers.
Chemical Composition
| C | Si | Mn | P | S | Cr | Ni |
| ≤0.070 | ≤0.75 | ≤2.00 | ≤0.040 | ≤0.015 | 17.50-19.00 | 8.00-10.00 |
Mechanical properties
| Hardness | Tensile strength(Min) | Yield Strength(Min) | Elongation(Min)% | Hardness | ||
| Mpa | Mpa | ＜0.4mm | 0.4-0.8mm | ≥0.8mm | HV(Min） | |
| 1/2 H | 860 | 515 | 10 | 10 | 12 | 250 |
| 3/4 H | 1035 | 760 | 6 | 7 | 7 | 310 |
| Applications | Tableware /Household appliances /Industry /Construction /decoration | ||||||||
| Mechanica Properties After Cold Rolling and Final Annealing | Rp0.2 | > 230 N/mm2 | |||||||
| Rm | 540 - 750 N/mm2 | ||||||||
| Elongation | > 45% | ||||||||
| Hardness | < 200 HB | ||||||||
| Physical Properties | 20℃ | 100℃ | 200℃ | 300℃ | 400℃ | 500℃ | |||
| Modulus of elasticity (GPa) | 200 | 194 | 186 | 179 | 172 | 165 | |||
| Mean coefficient of linear expansion between 20℃ (10-6 x K-1) and | - | 16 | 16.5 | 17 | 17.5 | 18 | |||
| Thermal conductivity (W/m·K) | 15 | 17 | 18 | 19 | 20.5 | 22 | |||
| Electrical resistivity (Ω·mm2/m) | 0.73 | 0.8 | 1 | 1.15 | 1.22 | 1.25 | |||
| WELDING | 304 is suitable for all conventional welding techniques.This grade does not require thermal treatment after welding. | N/A | |||||||
| PITTING CORROSION | 304 is successfully used in media where chloride concentration does not exceed 200 ppm. | N/A | |||||||
| CORROSION RESISTANCE | 304 shows good corrosion resistance in a wide range of applications. As an example, 304 exhibits corrosion rates lower than 0.10 mm/year in the following media: -20% acetic acid at 800C. -90% formic acid at 200C. -20% phosphoric acid at 600C. -20% nitric acid at 500C. -90% sulphuric acid at 200C. -Toluene. -Milk. -Beer. -Juice. -Wine. | ||||||||
| SURFACE CLEANING | Wash the surface with neutral soap and water applied with a cloth or a brush without scratching the stainless steel. Then, always rinse the stainless steel with water to remove completely the cleaning agent. Finally, it is recommended to dry the surface to preserve a good superficial condition. In severe environments, a frequent cleaning is strongly recommended. | ||||||||
| SPECIFICATIONS | 304 can be delivered according to EN, ASTM, ASME, AMS, QQS and MILS standard requirements. | ||||||||
| 304 is approved in compliance with: -PED (Pressure Equipment Directive), DGRL 97/23/EG according to EN 10028-7 and AD2000 Merkblatt W2 and W10. -Lloyd´s Register of Shipping. | |||||||||
| It complies with the European Directives: -Food industry, RE 1935/2004. -Hexavalent chromium, ROHS. -Electrical instruments, ROHS. | |||||||||